鋁卷如何防止氧化。

How to prevent oxidation of aluminum coils.

1.鋁板的貯存環(huán)境應干燥，明亮，通風良好，無腐蝕氣候。

1. The storage environment for aluminum plates should be dry, bright, well ventilated, and free of corrosive weather.

2.鋁卷應盡量避開漏雨，雪的地方。

2. Aluminum coils should be kept away from areas with rain or snow as much as possible.

3.加強軋制油的管理，其含水量控制在百分之零點零四以下。

3. Strengthen the management of rolling oil, and control its moisture content below 0.04%.

4.鋁卷的包裝應采用密封包裝，同時每卷應放入適量的干燥劑。

4. The packaging of aluminum coils should be sealed, and each coil should be filled with an appropriate amount of desiccant.

5.由低溫區(qū)運入溫度高，濕度大的地區(qū)時，不要立即開啟密封包裝。

When transporting from a low-temperature area to an area with high temperature and humidity, do not immediately open the sealed packaging.

6.包裝箱的木軸，箱板的濕度不大于18%，包裝彩色鋁卷的溫度不大于45℃，鋁卷。

6. The humidity of the wooden shaft and board of the packaging box shall not exceed 18%, and the temperature of the colored aluminum coil for packaging shall not exceed 45 ℃.

7.鋁卷在貯存時，嚴禁與化學材料和潮濕性材料一同存放。

7. When storing aluminum coils, it is strictly prohibited to store them together with chemical materials and humid materials.

鋁卷是一種常見的金屬產(chǎn)品，這種產(chǎn)品在工業(yè)上是有很大的需求量的，鋁卷在工業(yè)上的主要的角色是原材料，需要經(jīng)過各種各樣的加工之后，才能在市場上流通，鋁卷在市場上的規(guī)格以及型號也是非常的豐富的，基本上的需求都是能夠被滿足的，鋁卷在市場上的市場上也是有很多。

Aluminum coil is a common metal product that has a high demand in industry. The main role of aluminum coil in industry is raw material, which needs to be processed in various ways before it can circulate in the market. The specifications and models of aluminum coil in the market are also very diverse, and basic needs can be met. There are also many aluminum coils in the market.

如果鋁卷是放在木箱里面的，那么我們要保證木箱的濕度要小于18%，鋁卷而且鋁卷的溫度不能高于45℃。

If the aluminum coil is placed inside a wooden box, we need to ensure that the humidity of the wooden box is less than 18%, and the temperature of the aluminum coil cannot exceed 45 ℃.

如果在放置期間突然由低溫區(qū)域轉(zhuǎn)到高溫區(qū)域，那么我們不要立即將包裝打開，因為這樣很容易出現(xiàn)氧化的情況，我們應該等到鋁卷適用之后在進行拆封，這樣就不會出現(xiàn)氧化的情況。

If the packaging suddenly switches from a low temperature area to a high temperature area during storage, we should not immediately open it because it is prone to oxidation. We should wait until the aluminum coil is suitable before opening it, so that oxidation will not occur.

鋁卷板在生產(chǎn)過程中會出現(xiàn)各種各樣的質(zhì)量問題，造成質(zhì)量問題的原因是什么。

Various quality problems may occur during the production process of aluminum coil plates, and what are the reasons for these quality problems.

1，非金屬壓入。

1. Non metallic pressing.

主要原因：軋制工序設備條件不清凈，軋制工藝潤滑劑不清靜，工藝潤滑劑噴射壓力不足，板坯表面有擦劃傷。

Main reasons: Unclean equipment conditions in the rolling process, unclear lubricants in the rolling process, insufficient spraying pressure of process lubricants, and scratches on the surface of the slab.

2，擦傷。

2. Scratches.

主要原因：板，帶在加工生產(chǎn)過程中與導路，設備接觸時，產(chǎn)生相對摩擦而造成擦傷，冷軋卷端面不齊正，在立式爐退火翻轉(zhuǎn)時產(chǎn)生錯動，層與層之間產(chǎn)生擦傷，冷軋時張力不當，開卷時產(chǎn)生層間錯動而產(chǎn)生擦傷，精整驗收或包裝操作不當產(chǎn)生板間滑動而造成擦傷。

Main reasons: During the processing and production process, the plates and strips come into contact with the guides and equipment, causing relative friction and scratches. The end face of the cold-rolled coil is uneven, causing misalignment during annealing and flipping in a vertical furnace, resulting in scratches between layers. Improper tension during cold rolling causes interlayer misalignment and scratches during uncoiling, and improper finishing acceptance or packaging operations cause sliding between plates and scratches.

3，碰傷。

3. Collision injury.

主要原因：板，卷在搬運或存放過程中與其他物體碰撞產(chǎn)生，板，卷在退火料架或底盤上有其他突出物頂撞而產(chǎn)生，鋁卷。

Main reasons: collision between plates and coils and other objects during transportation or storage, and collision with other protrusions on the annealing material rack or chassis, resulting in aluminum coils.

本文由鋁卷生產(chǎn)廠家提供幫助，更多的相關內(nèi)容請點擊http://www.igugo.cn 希望本文能夠為您帶來幫助，感謝您的閱讀！

This article is provided by aluminum coil manufacturers for assistance. For more related content, please click on http://www.igugo.cn I hope this article can be helpful to you. Thank you for reading!