釬焊板和建筑用面板的加工你了解嗎?

來(lái)源:http://igugo.cn/ 發(fā)布時(shí)間:2020-04-08

  論述了鋁板生產(chǎn)廠家對(duì)釬焊板和建筑用面板的加工方法
  This paper discusses the processing methods of brazed plate and building panel by aluminum plate manufacturers
  1.熱交換器釬焊板(涂敷)
  1. Heat exchanger brazing plate (coating)
  真空釬焊散熱器用的W31C合金是由鋁板制造商開(kāi)發(fā)的。該合金是由1-m n-sn合金作為散熱器的核心材料和4005合金(ai-9.8% si-0.6% Mg)作為兩側(cè)的熔覆層組成。傳統(tǒng)上,鋁鋅合金7072是散熱器的核心材料。它作為功能陽(yáng)極,防止上部管道的腐蝕。但是,這種合金中的鋅會(huì)發(fā)絲,所以不適合制作真空散熱器。在W31C合金中,錫代替了傳統(tǒng)散熱器和鐵芯中的鋅。該合金已成功開(kāi)發(fā)并廣泛應(yīng)用于管道材料的陽(yáng)極真空釬焊散熱器的生產(chǎn)中。

鋁板生產(chǎn)廠家
  W31c alloy for vacuum brazing radiator is developed by aluminum plate manufacturer. The alloy is composed of 1-m n-sn alloy as the core material of radiator and 4005 alloy (ai-9.8% si-0.6% Mg) as the cladding layer on both sides. Traditionally, aluminum zinc alloy 7072 is the core material of radiator. It serves as a functional anode to prevent the corrosion of the upper pipe. However, the zinc in this alloy can hair, so it is not suitable for making vacuum radiator. In w31c alloy, tin replaces zinc in traditional radiator and iron core. The alloy has been successfully developed and widely used in the production of anode vacuum brazing radiator for pipeline materials.
  這些釬焊板的厚度為0.13x0.16毫米。板的晶粒尺寸限制在100微米以上,以防止在釬焊過(guò)程中硅從包層過(guò)度擴(kuò)散到芯材中。
  The thickness of these brazed plates is 0.13x0.16mm. The grain size of the plate is limited to more than 100 microns to prevent excessive diffusion of silicon from the cladding to the core during brazing.
  2.為建筑面板制作著色面板或陽(yáng)極化面板
  2. Make colored or anodized panels for building panels
  工業(yè)純鋁1050、1100和al-mg 5005因其與6063擠壓型材經(jīng)陽(yáng)極氧化著色后的優(yōu)異光澤度而得到廣泛應(yīng)用。陽(yáng)極氧化后表面出現(xiàn)條紋是一種常見(jiàn)的缺陷。由于這些缺陷對(duì)應(yīng)于鑄錠中的不均勻金相缺陷,如極性樹(shù)狀組織或懸浮晶體,因此可以通過(guò)控制鑄造過(guò)程來(lái)防止這些缺陷。
  Industrial pure aluminum 1050, 1100 and Al Mg 5005 are widely used because of their excellent glossiness after anodizing and coloring with 6063 extruded profiles. It is a common defect that there are stripes on the surface after anodizing. Because these defects correspond to inhomogeneous metallographic defects in ingots, such as polar dendrite or suspended crystal, these defects can be prevented by controlling the casting process.
  以上是鋁板生產(chǎn)廠家為大家介紹的相關(guān)內(nèi)容,想要了解更多內(nèi)容,歡迎訪問(wèn)網(wǎng)站:http://igugo.cn
  The above is the relevant content introduced by the aluminum plate manufacturer for you. To learn more, please visit the website: http://www.jndclyxgs.com

看黄色小说和视频免费| 鼻窦炎药图片大全| 日本调教一区二区三区免费| 一区 二区 自拍偷拍| 一本道之一区二区| 欧美大香蕉伊人综合| 亚洲欧美日韩黄片| 美女裸大逼逼视频| 日本人体一区二区三区四区| 99.人妻精品| 啪啪啪啪啪啪啪亚洲| 国外1区2区3区黄片| 日韩熟女黄片| 国产人妻精品一区二区秋霞| 日韩不卡一区二区操不停| 夜夜激情夜夜| 国产亚洲AV老师在线| 亚洲欧美一区三区三级| 日韩久久久久久久久久黄色电影| 双性操逼在线观看| 韩国电影麻豆久久| 欧美日韩精品一道本| 裸体美女老师一区二区三区毛片| 欧美精品 国内精品| 亚洲AⅤ97无码精品色| 欧美一级α视| 大香蕉日本一二三| 人妻偷拍日韩电影| 欧美日韩成人在线撸| 国产精品美女久久久久久久| 亚洲第一欧美激情| 超频 人人 麻豆| 91精品国产91久久久久久吃药 | 91视频国产精华| 成人片亚洲香蕉视频| 黑丝高潮喷水内射| 啪一啪 一区| 日韩午夜福利激情| 性aV三区| 欧美图片视频三区| 欧美极品免费专区激情在线|